WQ235 10 inch Carbon Steel Pipe
introduction
◆ Standards
| Q235 10 inch Carbon Steel Pipe | GB | ASTM | DIN | JIS | ISO |
| Q235A | Gr.D | SS440 SM400A | E235B | ||
| Q235B | S235JR S235JRG1 S235JRG2 | ||||
| Q235C | Gr.D Gr.65 | S235JO | SM400A SM400B | E235C | |
| Q235D | Gr.D | S235J2G3 S235J2G4 | SM400A | E235D |
◆ Properties
Chemical properties:
| Q235 Pipe | Grade | C | Si | Mn | P | S |
| A | ≤0.22 | ≤0.35 | ≤1.40 | ≤0.045 | ≤0.050 | |
| B | ≤0.20 | ≤0.045 | ||||
| C | ≤0.17 | ≤0.040 | ≤0.040 | |||
| D | ≤0.035 | ≤0.035 |
Mechancal properties:
| Q235 Steel Pipe | Grade | Yield Strength ReH/(N/mm2) | Tensile strength Rm/(N/mm2) | Elongation after break A/% | ||
| Thickness (or diameter)/mm | Thickness (or diameter)/mm | |||||
A B C D | ≤16 | ≥235 | 370~500 | ≤40 | ≥26 | |
| ＞16~40 | ≥225 | ＞40~60 | ≥25 | |||
| ＞40~60 | ≥215 | ＞60~100 | ≥24 | |||
| ＞60~100 | ≥215 | ＞100~150 | ≥22 | |||
| ＞100~150 | ≥195 | ＞150~200 | ≥21 | |||
| ＞150~200 | ≥185 | |||||
| Q235 Carbon Steel Pipe | Grade | Impact test (V-notch) | |
| temperature/℃ | Impact absorption energy (longitudinal)/J | ||
| A | - | ||
| B | +20 | 27 | |
| C | 0 | ||
| D | -20 | ||
| Q235 10 inch Carbon Steel Pipe | Specimen Direction | Cold bending test 180° B=2α | |
| Steel thickness (or diameter) / mm | |||
| ≤60 | ＞60~100 | ||
| Center diameter d | |||
| vertical | 0.5α | 1.5α | |
| horizontal | α | 2α | |
◆ Characteristic
Q235 10 inch carbon steel pipe, also known as A3 steel, is a common carbon structural steel.Q represents the yield limit of this carbon steel pipe, and the latter 235 refers to the yield value of this carbon steel pipe, which is about 235MPa.
But the yield value of Q235 pipe will decrease with the increase of thickness. Due to the moderate carbon content of Q235 steel pipe, good comprehensive performance, good matching of strength, plasticity and welding performance, Q235 steel pipe is the most widely used.
◆ Industry&Application
Q235 10 inch carbon steel pipes have the largest output and are widely used. They are mainly used in building structures such as factories, bridges, ships, and general pipelines for conveying fluids.Q235 carbon steel pipes are generally used directly without heat treatment.
Q235 10 inch carbon steel pipe can be used to transport low-pressure fluid, and Q235 steel pipe can also be used to manufacture various abrasive tool handles and other unimportant abrasive tool parts.Q235 pipe is used as the punch material, which can be used directly without tempering after quenching. The hardness is 36~40HRC, which solves the phenomenon that the punch is broken during use.
◆ Purchasing Information
| Product name | Q235 Sch40 10 inch Carbon Steel Pipe | ||||
|
Grade |
Q195 = S195 / A53 Grade A |
||||
|
Q235 = S235 / A53 Grade B / A500 Grade A / STK400 / SS400 / ST42.2 |
|||||
|
Q345 = S355JR / A500 Grade B Grade C |
|||||
|
Outer Diameter |
ERW / HFW |
LSAW / DSAW |
SSAW / HSAW |
RHS |
SHS |
|
1/8 - 20 inch |
12 - 56 inch |
8 - 126 inch |
40 x 20 mm |
15 x 15 mm |
|
|
(10.3-508 mm) |
(323.8-1,420 mm) |
(219.1-3,200 mm) |
-1,000 x 800 mm |
-1,000× 1,000 mm |
|
|
Wall Thickness |
0.4 - 16 mm |
6.0 - 40 mm |
6.0 - 26 mm |
1.0 - 30 mm |
0.6 - 30 mm |
|
Length |
5.8~12.0 m or as customized |
||||
|
Surface Treatment |
Prime quality (bared, oiled, color paint, 3LPE, or other anti-corrosive treatment) |
||||
|
Inspection |
With Chemical Composition and Mechanical Properties Analysis; |
||||
| Dimensional and Visual Inspection, also with Nondestructive Inspection. | |||||
| *If you do not find what you are
looking for, please call us now. If you have found it, we are happy to
answer any questions or concerns you may have about stainless steel
grades and assist you through the purchasing process. | |||||
hot product